Incoloy 926 alloy(UNS N08926/W.Nr.1.4529)板材,带材,线材,棒材,丝材 |
合金926是一种超奥氏体钼不锈钢,具有良好的耐多种高腐蚀性环境。钼和氮的组合在其组成抗点蚀和裂隙腐蚀,而铜提高耐硫酸,氮提高产量和拉伸强度。 |
Incoloy 926 alloy(UNS N08926/W.Nr.1.4529)化学成份 |
|
|
|
|
|
|
|
| Ni | Cu | Mn | C | Si | S | Cr | Mo | Fe | P | N |
最小 | 24 | 0.5 |
|
|
|
| 19 | 6 |
|
| 0.15 |
最大 | 26 | 1.5 | 2 | 0.02 | 0.5 | 0.01 | 21 | 7 | Bal | 0.03 | 0.25 |
|
|
|
|
|
|
|
|
|
|
|
|
Incoloy 926 alloy(UNS N08926/W.Nr.1.4529)化学成份 |
|
|
|
|
|
|
|
抗拉强度 | 屈服强度 | 延伸率 | 收缩率 | 硬度 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
ó bMpa | ó 0.2Mpa | δ5% | Ψ% | RB |
|
|
|
|
|
|
|
690 | 330 | 42 |
| 86 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Incoloy 926 alloy(UNS N08926/W.Nr.1.4529)腐蚀条件 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
腐蚀条件 | 温度 | 腐蚀率 |
| 腐蚀条件 | 温度 | 腐蚀率 |
|
|
|
Myp | mm/a | Myp | mm/a |
|
|
|
0.2%HCI | 沸腾 | <0.10 | <0.00 | 60.0%H2SO4 | 70 | 9.4 | 0.24 |
|
|
|
1.0%HCI | 90 | 37 | 0.94 | 30 | 6 | 0.15 |
|
|
|
70 | 0.02 | <0.00 | 95.0%H2SO4 | 50 | 18.9 | 0.48 |
|
|
|
5.0%HCI | 50 | 43.4 | 1.1 | 30 | 12.5 | 0.32 |
|
|
|
30 | 10.6 | 0.27 | 85.0%H3PO4 | 90 | 0.24 | 0.01 |
|
|
|
10.0%H2SO4 | 沸腾 | 10.4 | 0.26 | 80.0%HC2H3O2 | 沸腾 | <0.10 | <0.00 |
|
|
|
70 | 2.5 | 0.06 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Incoloy 926 alloy(UNS N08926/W.Nr.1.4529)规范. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
棒材,线材,锻件- ASTMB166、ASMESB166、SAEAMS5887、ISO9723、ISO9724、ISO9725、DIN17752、DIN17753、DIN17754 |
|
|
|
|
|
|
|
|
|
|
|
|
热轧板,冷轧板,带材- ASTMB168、ASMESB168、ISO6208、DIN17750 |
|
|
|
|
|
|
|
|
|
|
|
|
输送管,管子ISO6207、ASTMB167、ASMESB167、ASTMB751、ASMESB751、ASTMB775、ASMESB775、ASTMB829、ASMESB829、DIN17751 |
|
|
|
|
|
|
|
|
|
|
|
|
焊接产品-AWSA5.14/ERNiCrFe-10 |